Praseodymium sulfate was obtained by the precipitation method and the crystal structure was determined by Rietveld analysis. Pr₂(SO₄)₃ is crystallized in the monoclinic structure, space group <i>C</i>2/<i>c</i>, with cell parameters <i>a</i> = 21.6052 (4), <i>b</i> = 6.7237 (1) and <i>c</i> = 6.9777 (1) Å, β = 107.9148 (7)°, <i>Z</i> = 4, <i>V</i> = 964.48 (3) ų (<i>T</i> = 150 °C). The thermal expansion of Pr₂(SO₄)₃ is strongly anisotropic. As was obtained by XRD measurements, all cell parameters are increased on heating. However, due to a strong increase of the monoclinic angle β, there is a direction of negative thermal expansion. In the argon atmosphere, Pr₂(SO₄)₃ is stable in the temperature range of <i>T</i> = 30–870 °C. The kinetics of the thermal decomposition process of praseodymium sulfate octahydrate Pr₂(SO₄)₃·8H₂O was studied as well. The vibrational properties of Pr₂(SO₄)₃ were examined by Raman and Fourier-transform infrared absorption spectroscopy methods. The band gap structure of Pr₂(SO₄)₃ was evaluated by ab initio calculations, and it was found that the valence band top is dominated by the p electrons of oxygen ions, while the conduction band bottom is formed by the d electrons of Pr³⁺ ions. The exact position of ZPL is determined via PL and PLE spectra at 77 K to be at 481 nm, and that enabled a correct assignment of luminescent bands. The maximum luminescent band in Pr₂(SO₄)₃ belongs to the ³P₀ → ³F₂ transition at 640 nm.