Ag4Bi2O5/MnO2 nano-sized material was synthesized by a co-precipitation method in concentrated KOH solution. The morphology characterization indicates that MnO2 nanoparticles with a size of 20 nm are precipitated on the surface of nano Ag4Bi2O5, forming a structure like corn on the cob. The obtained material with 60% Mn offers slightly higher initial potential (0.098 V vs. Hg/HgO) and limiting current density (−5.67 mA cm−2) at a rotating speed of 1600 rpm compared to commercial Pt/C (−0.047 V and −5.35 mA cm−2, respectively). Furthermore, the obtained material exhibits superior long-term durability and stronger methanol tolerance than commercial Pt/C. The remarkable features suggest that the Ag4Bi2O5/MnO2 nano-material is a very promising oxygen reduction reaction catalyst.