Find in Library

The microstructure of ferroelectric hafnium oxide plays a vital role for its application, e.g., non-volatile memories. In this study, transmission Kikuchi diffraction and scanning transmission electron microscopy STEM techniques are used to compare the crystallographic phase and orientation of Si and Zr doped HfO₂ thin films as well as integrated in a 22 nm fully-depleted silicon-on-insulator (FDSOI) ferroelectric field effect transistor (FeFET). Both HfO₂ films showed a predominately orthorhombic phase in accordance with electrical measurements and X-ray diffraction XRD data. Furthermore, a stronger texture is found for the microstructure of the Si doped HfO₂ (HSO) thin film, which is attributed to stress conditions inside the film stack during crystallization. For the HSO thin film fabricated in a metal-oxide-semiconductor (MOS) like structure, a different microstructure, with no apparent texture as well as a different fraction of orthorhombic phase is observed. The 22 nm FDSOI FeFET showed an orthorhombic phase for the HSO layer, as well as an out-of-plane texture of the [111]-axis, which is preferable for the application as non-volatile memory.