Grain Boundary Evolution of Cold-Rolled FePd Alloy during Recrystallization at Disordering Temperature
oleh: Hung-Pin Lin, Delphic Chen, Jui-Chao Kuo
Format: | Article |
---|---|
Diterbitkan: | MDPI AG 2015-06-01 |
Deskripsi
In this study, the grain boundary character and texture of 50% and 90% cold-rolled FePd alloy was investigated during recrystallization at 700 °C. Electron backscatter diffraction (EBSD) measurements were performed on the rolling direction to normal direction section. Kernel average misorientation (KAM) calculated from EBSD measurements was employed to determine the recrystallization fraction. The Avrami exponent n of recrystallization is 1.9 and 4.9 for 50% and 90% cold rolling, respectively. The new formation of texture reveals random texture during the recrystallization process. As annealing time increased, the number of high angle boundary (HAGB) and coincidence site lattice (CSL) increased with consumption of low angle boundary (LAGB). In addition, possible transformations between different grain boundaries are observed here.