The present study attempts to provide insights for both the chemical composition (Si/Al) and the crystal morphology of ZSM-5 zeolites while using biomass template compounds in the synthesis. The solution containing biomass-derivative compounds was obtained after treating biomass in a sodium hydroxide aqueous solution under reflux. The latter alkaline solution was used as a solvent for zeolite nuclei ingredients to form the gel phase under hydrothermal conditions (170 °C during 24, 48 or 72 h). This approach allowed for preparing MFI zeolites having a broad range of Si/Al ratio, i.e., from 25 to 150. Likewise, MFI crystals with different morphologies could be obtained, being different from the pristine zeolite formed in the absence of biomass.