Typical penny-shaped microcracks at their propagating in spallation of Zr-based bulk metallic glass (Zr-BMG) samples were captured by a specially designed plate impact technique. Based on the morphology and stress environment of the microcrack, a damaged zone or propagation zone around the crack tips, similar to the cohesive zone in classical fracture theories, is applied. Especially the scale of such a damaged zone represents a scale of the crack propagation. Its fast propagation would quickly bring a longer crack or cause cracks coalesce to form another longer one. The estimated propagation scales of microcracks are reasonable compared with what occurred in the Zr-BMG samples.