Find in Library

The strong hygroscopicity of wood greatly shortens its service life. Here, a simple impregnation modification approach was used to construct superhydrophobic silicone resin coatings on wood surfaces. Briefly, with hydrofluorosilicone oil (HFSO), tetramethyl tetravinyl cyclotetrasiloxane (V₄), and hydrophobic SiO₂ from industrial production as raw materials, superhydrophobic wood samples (water contact angle ~160.8°, sliding angle ~3.6°) can be obtained by simply dipping the wood in the HFSO/V₄/SiO₂ modifier solutions. As a result, the superhydrophobic silicone resin coating constructed on the wood surface still has good water repellency after finger touching, tape peeling, and sandpaper abrasion. When the mass ratio of HFSO to V₄ is 2:1, the water absorption of the resulting wood after soaking in water for 24 h is only 29.2%. Further, the resulting superhydrophobic wood shows excellent anti-fouling properties. Finally, we believe that the impregnation modification method proposed in this study can be applied to the protection of cellulose substrates.