Find in Library

The microstructure and mechanical properties of magnesium (Mg) alloys are signifi cantly infl uenced by the casting process. In this paper, a comparative study on microstructure and mechanical properties at ambient and elevated temperatures of AZ91-2wt.% Ca (AZX912) Mg alloy samples prepared by gravity casting (GC), squeeze casting (SC) and rheo-squeeze casting (RSC), respectively, was carried out. The results show that α-Mg grains in SC and RSC samples are signifi cantly refi ned compared to the GC sample. The average secondary dendritic arm spacing of AZX912 alloy samples decreases in the order of GC, SC and RSC. As testing temperature increases from 25 °C to 200 °C, strength of AZX912 alloy samples is reduced, while their elongation is increased continuously. Compared to GC and SC processes, RSC process can improve the mechanical properties of AZX912 alloy at both ambient and elevated temperatures. The enhancement of mechanical properties of RSC sample over GC and SC samples mainly results from grain refi nement in the as-cast microstructure of AZX912 alloy.