Find in Library

A novel dual-phase PHSS consisting of lath martensite plus allotriomorphic δ ferrite (ALF) with nanoprecipitates was characterized by high-resolution field emission transmission electron microscopy for quenched, solid-solution-treated, and aged stainless steel. The effects of aging at various durations prior to H₂O or liquid N₂ quenching were investigated. Cu-rich nanoprecipitates evolve from body-centered cubic clusters to 9R Cu under quenching to 3R Cu and subsequently to face-centered cubic ε-Cu at various aging durations. Maximum hardness was observed after aging at 600 °C for 1 h. However, after this aging, both reversed austenite and Cu-rich nanoprecipitates coexisted in the martensite matrix. The segregation and diffusion of austenite-stabilizing elements promoted the nucleation of reversed austenite.