Find in Library

High-pressure torsion was used to process grade 2 titanium to 10 turns using different pressures up to a maximum of 8 GPa. X ray diffraction showed that the as-received material and the material processed at pressures of 2 GPa and 4 GPa were single phase but the material processed at 8 GPa contained both the h.c.p. and the simple hexagonal ω-phase. Nanoindentation was used to determine the mechanical behavior and the results show a pronounced increase in hardness due both to the severe plastic deformation processing and to the phase transformation at the highest pressure. A maximum hardness of ~4.7 GPa was attained.