The nanocaps array of TiO2/Ag bilayer with different Ag thicknesses and co-sputtering TiO2-Ag monolayer with different TiO2 contents were fabricated on a two-dimensional colloidal array substrate for the investigation of Surface enhanced Raman scattering (SERS) properties. For the TiO2/Ag bilayer, when the Ag thickness increased, SERS intensity decreased. Meanwhile, a significant enhancement was observed when the sublayer Ag was 10 nm compared to the pure Ag monolayer, which was ascribed to the metal-semiconductor synergistic effect that electromagnetic mechanism (EM) provided by roughness surface and charge-transfer (CT) enhancement mechanism from TiO2-Ag composite components. In comparison to the TiO2/Ag bilayer, the co-sputtered TiO2-Ag monolayer decreased the aggregation of Ag particles and led to the formation of small Ag particles, which showed that TiO2 could effectively inhibit the aggregation and growth of Ag nanoparticles.