The aim of this study is to investigate a characteristic deformation behavior of a precipitation strengthening-type Cu-Ni-Si alloy (Cu-2.4Ni-0.51Si-9.3Zn-0.15Sn-0.13Mg) by microcompression specimens. Three micropillars with a square cross-section of 20 × 20 × 40 μm³ were fabricated by focused ion beam (FIB) micromachining apparatus and tested by a machine specially designed for microsized specimens. The three pillars were deformed complicatedly and showed different yield strengths depending on the crystal orientation. The micromechanical tests revealed work hardening by the precipitation clearly. Electron backscattered diffraction analysis of a deformed specimen showed a gradual rotation of grain axis at the grain boundaries after the compression test.