Find in Library

ZrN-Cu coatings containing two different amounts of Cu (~11 at.% and ~25 at.%) were deposited using an industrial physical vapor deposition (PVD) system. The as-deposited coatings exhibited 100% bactericidal efficiency against <i>Escherichia coli</i> CCM 3988 for an exposure time of 40 min. Subsequently, the samples were attached onto our faculty’s door handles for six months to study the coatings’ long-term effectiveness and durability under actual operational conditions. The samples were periodically evaluated and it was observed that the coatings with 25 at.% Cu performed better than the ones with 11 at.% Cu. For example, following 15 days of being touched, the bactericidal effectiveness of the sample containing 25 at.% Cu dropped to 65% while it fell to 42% for the sample containing 11 at.%. After 6 months, however, both samples showed bactericidal efficiency of ~16–20%. The bactericidal efficiency of the samples touched for 6 months was successfully restored by polishing them. Furthermore, a group of samples was kept untouched and was also evaluated. The untouched samples with Cu content of ~25 at.% did not show any drop in their bactericidal properties after 6 months. ZrN-Cu coatings were concluded to be promising materials for self-sanitizing application on high-touch surfaces.