Find in Library

This work analyzed changes in the corrosion morphology and mechanical performance of 7085 aluminum alloy after outdoor exposures for different times in a humid and hot marine atmospheric environment. After one month of exposure, a pronounced corrosion of the alloy was observed. The corrosion product was mainly Al(OH)₃, and the corrosion features were mainly pitting corrosion and intergranular corrosion (IGC). With the exposure time extended from 6 months to 12 months, the IGC depth increased from 114 μm to 190 μm. After a 1-year outdoor exposure in a humid and hot marine environment, the alloy’s ultimate strength and yield stress remained nearly unchanged, while its elongation and area reduction decreased from the original 6% and 9%, respectively, to 3% and 5%. Moreover, the reasons for IGC and its effect on the mechanical performance was analyzed.