Sedimentation studies have been carried out to optimize the dispersion conditions of aqueous alumina nanopowder suspensions with or without dispersants (ammonium salt of polymethacrylic acid or rhamnolipids at 15%). Different dispersant dosages, solid loadings, pulp densities and pH values were examined. The iso-electric point (IEP) of the alumina nanopowder was found to be pHiep= 9.2. The experiments revealed that the polymethacrylic acid was more effective as dispersant than rhamnolipids in a wide range of pH at all solid-loading conditions tested. Optimum dispersant dosages for polymethacrylic acid and rhamnolipids to achieve maximum stability of alumina nanodispersion at iso-electric point were found to be 9.25 mg/g and 57.75 mg/g solids, respectively.<br>Foram feitos estudos de sedimentação para otimizar as condições de dispersão de suspensões aquosas de pós de alumina nanométrica com e sem dispersantes (sais de amônia de ácido poliacrílico ou rhamnolipídeos a 15%). Foram examinados diferentes dosagens de dispersante, cargas de sólidos, densidades de pasta e valores de pH. O ponto isoelétrico do pó de alumina nanométrica obtido foi pHiep = 9,2. Os experimentos mostraram que numa ampla faixa de pH e para todas as condições de carga de sólidos testadas, o ácido polimetacrílico foi mais efetivo como dispersante que o rhamnolipídeo. Os teores otimizados de dispersante para que as dispersões de alumina nanométrica atinjam estabilidade máxima, obtidos para o ácido polimetacrílico e para o rhamnolipídeo foram, respectivamente, 9,25 mg/g e 57,75 mg/g de sólidos.