In this report, we studied the thickness effect on the optical and morphological properties of self-assembled (SA) poly(p-phenylenevinylene) (PPV) films, wich were processed with 5 and 75 layers from a PPV precursor polymer and dodecylbenzenesulfonate, and then, thermally converted at 230 °C. The increase of the film thickness yielded more intense peaks in the vibrational spectral range. The electron-phonon coupling was quantified by the Huang - Rhys factor, that shows the effects on the polymer chain mobility in the interface substrate/polymer. A strong emission anisotropy r=0.57 was observed for the film with 5 layers of thickness decreasing to 0.34 for the film with 75 layers. Finally, the surface topology of the films was measured using Atomic Force Microscopy.