Development and Mechanical Characterisation of Al6061-Al<sub>2</sub>O<sub>3</sub>-Graphene Hybrid Metal Matrix Composites

oleh: Satish Babu Boppana, Samuel Dayanand, Bharath Vedashantha Murthy, Madeva Nagaral, Aravinda Telagu, Vijee Kumar, Virupaxi Auradi

Format: Article
Diterbitkan: MDPI AG 2021-06-01

Deskripsi

MMC based on aluminium (Al) were produced for light-weight applications especially in aviation and automobile areas. Present paper deals with the fabrication and mechanical performance of AA6061 matrix composites fortified with Al<sub>2</sub>O<sub>3</sub> (alumina) and graphene particulates. Fluid metallurgy method namely stir casting route was employed for fabricating the hybrid composites. Al<sub>2</sub>O<sub>3p</sub> and graphene powder are mixed in different weight fractions in which graphene (1 wt. %) particle reinforcement is held consistent and Al<sub>2</sub>O<sub>3</sub> reinforcement is differed freely with 5, 10 and 15 wt. %. Using optical analyser and SEM equipment, microstructural examination is carried out and the result reveals that the graphene and Al<sub>2</sub>O<sub>3</sub> particles prevalently are homogeneously appropriated on the grain limits of Al matrix and Al<sub>2</sub>O<sub>3</sub> particles are disseminated between graphene in the as-cast AA6061 MMC’s. Detailed analysis on investigation of the microstructure and mechanical aspects of Al6061-graphene-Al<sub>2</sub>O<sub>3p</sub> composites is presented by following ASTM guidelines; results uncovered that with increment in reinforcement particles, there is an enhancement in the hardness, ultimate strength, yield strength and a decline in the elongation values was however noticed when contrasted with Al6061 alloy. Fractography investigation revealed dimples in unreinforced alloy and the composite.