Effects of processing parameters on the metallurgical defects, microstructure, texture, and mechanical properties of pure tungsten samples fabricated by selective electron beam melting are investigated. SEBM-fabricated bulk tungsten samples with features of lack of fusion, sufficient fusion, and over-melting are examined. For samples upon sufficient fusion, an ultimate compressive strength of 1.76 GPa is achieved at the volumetric energy density of 900 J/mm³–1000 J/mm³. The excellent compressive strength is higher and the associated volumetric energy density is significantly lower than corresponding reported values in the literature. The average relative density of SEBM-fabricated samples is 98.93%. No microcracks, but only pores with diameters of few tens of micrometers, are found in SEBM-ed tungsten samples of sufficient fusion. Properties of samples by SEBM and selective laser melting (SLM) have also been compared. It is found that SLM-fabricated samples exhibit inevitable microcracks, and have a significantly lower ultimate compressive strength and a slightly lower relative density of 98.51% in comparison with SEBM-ed samples.