Recurrent caries remain a persistent concern, often linked to microleakage and a lack of bioactivity in contemporary dental composites. Our study aims to address this issue by developing a low-shrinkage-stress nanocomposite with antibiofilm and remineralization capabilities, thus countering the progression of recurrent caries. In the present study, we formulated low-shrinkage-stress nanocomposites by combining triethylene glycol divinylbenzyl ether and urethane dimethacrylate, incorporating dimethylaminododecyl methacrylate (DMADDM), along with nanoparticles of calcium fluoride (nCaF₂) and nanoparticles of amorphous calcium phosphate (NACP). The biofilm viability, biofilm metabolic activity, lactic acid production, and ion release were evaluated. The novel formulations containing 3% DMADDM exhibited a potent antibiofilm activity, exhibiting a 4-log reduction in the human salivary biofilm CFUs compared to controls (<i>p</i> < 0.001). Additionally, significant reductions were observed in biofilm biomass and lactic acid (<i>p</i> < 0.05). By integrating both 10% NACP and 10% nCaF₂ into one formulation, efficient ion release was achieved, yielding concentrations of 3.02 ± 0.21 mmol/L for Ca, 0.5 ± 0.05 mmol/L for P, and 0.37 ± 0.01 mmol/L for F ions. The innovative mixture of DMADDM, NACP, and nCaF₂ displayed strong antibiofilm effects on salivary biofilm while concomitantly releasing a significant amount of remineralizing ions. This nanocomposite is a promising dental material with antibiofilm and remineralization capacities, with the potential to reduce polymerization-related microleakage and recurrent caries.